Synthesis, Structural, and Optical Properties of Modified Poly(vinyl Chloride) Thin Films by Ethylenediamine Loaded with Metal Oxide Nanoparticles

Poly (vinyl chloride) (PVC) films modified with ethylenediamine (en) and doped by nanoparticles (TiO2, ZnO, NiO, and MgO). A mixture of 0.5 g PVC/en dissolved in THF and 0.01 wt % of nanoparticles were used in doping PVC to produce the nanocomposite films. All modified PVC films were characterized by different analysis techniques such as Fourier Transform Infrared (FTIR), Nuclear Magnetic Resonance Spectrometer (NMR), diffusive reflectance spectroscopy (DRS), X-ray diffraction analysis (XRD), and scanning electron microscopy (SEM). The DRS was used to analyse the scattered IR energy of the samples at wavelengths between (250–1350 nm). The optical properties and oscillator strength were also studied, the transmittance and reflectance values declined for the PVC films, and the absorption coefficient was observed between (79–89 %). The direct energy gap decreased from 4.6 to 1.9, and the indirect energy gap reduced from 4.3 to 1.9. The XRD exhibited a semi-crystalline structure and the SEM test exhibited a porous structure of all samples. The Urbach energy was increased from 0.8772 eV to 14.712 eV, single oscillator energy ((Formula presented.)) was also increased from 6.38 eV to 13.69 eV and the dispersion energy (Formula presented.) increased from 23.40 eV to 70.63 eV. Moreover, the surface roughness parameters Ra and Rq of the PVC films in modified and doping were increased from 3.86 nm to 8.14 nm, and 5.08 nm to 10.10 nm respectively. So, PVC results show increased optical properties after modification with en and doping by NPs are used in the light conversion and aerospace industries.